Zheflon® FL2005 PVDF- Extrusion Grade

Zheflon® FL2005 PVDF- Extrusion Grade

Zheflon® FL2005 PVDF- Extrusion Grade
Zheflon® FL2005 PVDF- Extrusion GradeZheflon® FL2005 PVDF- Extrusion GradeZheflon® FL2005 PVDF- Extrusion Grade
CategoriesPVDF for others
AlbumView larger image
BrandFlurine
ModelFL2005
FeaturesHomopolymer, medium melt viscosity
UsesFishing line, OK line
FormsWhite translucent particles
Update Time2019-12-12
Detail Information


Zheflon® FL2005 is a medium-viscosity grade polyvinylidene fluoride homopolymer with high purity. Important properties include excellent chemical resistance to most aggressive substances and solvents, excellent mechanical strength and toughness, high abrasion resistance, high temperature capabilities, excellent aging resistance, low permeability to most gases and liquids and easily melt-processed by standard methods of squeeze and molding.


General

Features

Homopolymer, medium melt viscosity

Uses

Fishing line, OK line

Forms

White translucent particles

Items

Typical Value FL2005

Test Method

Physical Properties

Density(g/cc)

1.76~1.79

ASTM D792

Melt Flow Rate(g/10min)

1.5~2.5

Load 10kg,230℃,ASTM D1238

Melt viscosity(Kps)

21~25

Shear Rate 100 1/s,ASTM D3835

 

Water Absorption(%)(Time 24 hr)

≤0.010

ISO 62

Molecular Properties

Molecular weight(Da)

420,000~460,000

GPC,DMF,ISO 16014

Intrinsic viscosity(dl/g)

1.25~1.35

30℃,DMAC

Molecular weight distribution

1.8-2.3

GPC,DMF,ISO 16014

Mechanical Properties

Tensile Modulus(Thickness2.00mm)(MPa)

1800~2500

1.0mm/min,ASTM D638

Flexural Modulus(Thickness2.00mm)(MPa)

1700~2500

2.0mm/min,ASTM D790

Yield Strength(Thickness2.00mm)(MPa)

50.0~57.0

50mm/min,ASTM D638

Break Strength(Thickness2.00mm)(MPa)

20.0~50.0

50mm/min,ASTM D638

Elongation at Yield(%)

5.0~10

50mm/min,ASTM D638

Elongation at Break(%)

20~50

50mm/min,ASTM D638

Hardness, Shore D(Thickness2.00mm)

75~80

ASTM D2240

Thermal Properties

Melting Point(℃)

169~173

ASTM D3418

Crystallization temperature(DSC peak)(℃)

137~144

ASTM D3418

Glass Transition Temp, Tg(℃)

-32

ASTM E1356

Decomposition Temperature(℃)

375

1% wt. loss / in air

Vicat softening point(℃)

135~145

ASTM D1525

Heat distortion temperature 1.8 MPa

(Thickness 4.00mm)(℃)

100~120

After annealing 150℃,16h

ASTM D648

Electrical Performance

Surface resistance(ohm)

≥1.00E+14

Voltage<1V,After 2 min—500V

ASTM D257

Resistivity(ohm·cm)

≥1.00E+14

Intensity=10mA,After 2 min@23℃

ASTM D257

Dielectric strength(Thickness 1.00mm,23℃)(KV/mm)

20~25

ASTM D149

Dielectric constant(1kHz,23℃)

7.0~10.0

ASTM D150

Combustion performance

UL Flammability rating(0.100mm)

V-0

UL94

Oxygen Index(3.00mm)

44%

ASTM D2683


1.PVDF should be processed under 260℃,to avoid producing toxic gases;

2.PVDF has good fire resistance and smoke inhibition property, however, when meets with fire, it will release toxic hydrogen fluoride gas and fluorocarbon compounds;

3.Operators should take good care of personal protection during the use procedure and processing.


PVDF is packed in PE plastic bag and then be put into a drum with the net weight 25KGS. It must be stored in clean, cool, dry place.

Please send your message to us
*Email
Tel
*Title
*Content

Agree to use terms of service

Categories
Contact Person
leave a message:
Contact Now
Address:
No.5, Weiyi Road, Shangyu Hangzhou Gulf Chemical Industrial Zone,          Zhejiang, China 312369
subscription
Mobile page